Under what condition is galvanic corrosion most likely to occur?

Under what condition is galvanic corrosion most likely to occur?

• A. Similar metals in contact
• B. Different metals in contact
• C. In dry environments
• D. In low humidity

Answer: (B)

Galvanic corrosion is most likely to occur when different metals are in contact with each other in the presence of an electrolyte. This phenomenon arises from the electrochemical reaction that occurs due to the difference in the electrochemical potential between the two dissimilar metals. When these metals are connected electrically and exposed to moisture (as an electrolyte), one metal becomes anodic (corrodes) while the other becomes cathodic (protected). This can lead to accelerated corrosion of the more anodic (less noble) metal. In scenarios involving similar metals in contact, they tend to behave similarly in terms of corrosion potential, which greatly reduces the likelihood of galvanic corrosion occurring. For the other environmental conditions mentioned, such as dry environments and low humidity, they typically hinder the necessary electrochemical reactions that facilitate corrosion, thus further limiting the chances of galvanic corrosion. Therefore, the presence of two different metals in contact is a key condition that increases the risk of galvanic corrosion.

Galvanic corrosion is most likely to occur when different metals are in contact with each other in the presence of an electrolyte. This phenomenon arises from the electrochemical reaction that occurs due to the difference in the electrochemical potential between the two dissimilar metals. When these metals are connected electrically and exposed to moisture (as an electrolyte), one metal becomes anodic (corrodes) while the other becomes cathodic (protected). This can lead to accelerated corrosion of the more anodic (less noble) metal.

In scenarios involving similar metals in contact, they tend to behave similarly in terms of corrosion potential, which greatly reduces the likelihood of galvanic corrosion occurring. For the other environmental conditions mentioned, such as dry environments and low humidity, they typically hinder the necessary electrochemical reactions that facilitate corrosion, thus further limiting the chances of galvanic corrosion. Therefore, the presence of two different metals in contact is a key condition that increases the risk of galvanic corrosion.